Surface characterisation and bonding of Y-TZP following non-thermal plasma treatment

Guilherme B. Valverde, Paulo G. Coelho, Malvin N. Janal, Fábio Cesar Lorenzoni, Ricardo M. Carvalho, Van P. Thompson, Klaus Dieter Weltemann, Nelson R.F.A. Silva

Research output: Contribution to journalArticle

Abstract

Objectives: (1) To chemically characterise Y-TZP surface via X-ray photoelectron spectroscopy (XPS) and evaluate the surface energy levels (SE) after non-thermal plasma (NTP). (2) To test the microtensile bond strength (MTBS) of Y-TZP bonded to cured composite disks, after a combination of different surface conditioning methods. Methods: Twenty-four Y-TZP discs (13.5 mm × 4 mm) were obtained from the manufacturer and composite resin (Z-100) discs with similar dimensions were prepared. All discs were polished to 600 grit and divided into 8 groups (n = 3 disks each), four control (non-NTP treated) and four experimental (NTP treated for 10 s) groups. All groups received one of the four following treatments prior to cementation with Rely × Unicem cement: sand-blasting (SB), a Clearfil ceramic primer (MDP), sand-blasting + MDP (SBMDP), or baseline (B), no treatment. SE readings and surface roughness parameters were statistically analysed (ANOVA, Tukey's, p < 0.05). Mixed model and paired samples t-tests were used to compare groups on MTBS. Results: XPS showed increase in O and decrease in C elements after NTP. The polar component increased for BP (42.20 mN/m) and SBP (43.77 mN/m). MTBS values for groups BP (21.3 MPa), SBP (31 MPa), MDPP (30.1 MPa) and SBMDPP (32.3 MPa) were significantly higher in specimens treated with NTP than their untreated counterparts B (9.1 MPa), SB (14.4 MPa), MDP (17.8 MPa) and SBMDP (24.1 MPa). Conclusions: (1) Increase of O and decrease of C led to higher surface energy levels dictated by the polar component after NTP; (2) NTP application increased MTBS values of Y-TZP surfaces.

Original languageEnglish (US)
Pages (from-to)51-59
Number of pages9
JournalJournal of Dentistry
Volume41
Issue number1
DOIs
StatePublished - Jan 1 2013

    Fingerprint

Keywords

  • Adhesion
  • Contact angle
  • Microtensile
  • Non-thermal plasma
  • Surface energy
  • Y-TZP

ASJC Scopus subject areas

  • Dentistry(all)

Cite this

Valverde, G. B., Coelho, P. G., Janal, M. N., Lorenzoni, F. C., Carvalho, R. M., Thompson, V. P., Weltemann, K. D., & Silva, N. R. F. A. (2013). Surface characterisation and bonding of Y-TZP following non-thermal plasma treatment. Journal of Dentistry, 41(1), 51-59. https://doi.org/10.1016/j.jdent.2012.10.002