STM study of the surface morphology of gold on mica

Christopher E D Chidsey, Dominic N. Loiacono, Tycho Sleator, Sho Nakahara

    Research output: Contribution to journalArticle

    Abstract

    The scanning tunneling microscope (STM) promises to be a useful tool for the study of thin film deposition processes. We have imaged the growth surface of vapor-deposited gold on mica with an STM. Monatomic steps, dislocations, grain boundaries and grain topographies have been mapped for various gold thicknesses and deposition temperatures. Complementary X-ray diffraction and transmission electron microscopy experiments have been used to determine the orientation, size, shape and defectiveness of the crystallites. Near room temperature, the nuclei do not fuse together into larger single crystallites as the film coalesces, and the mounded topography of the individual crystallites evolves only slightly as the film thickens. The mounds are about 500 Å across and 75 Å high. At higher temperatures (150°C to 300°C), the nuclei apparently fuse as the film coalesces, giving larger crystallites containing holes. The dislocations observed by STM are apparently created as these holes fill in, due to frequent misregistry of the gold lattice around the holes. In the latter stages of deposition, there is a temperature-dependent flattening of the irregular topography caused by the island growth mode, which we attribute to surface diffusion. Consequently, starting the deposition at lower temperatures and increasing the temperature during the deposition gives very flat surfaces. In contrast, depositing gold under the same conditions on a thin underlayer of silver results in large islands separated by grooves, presumably due to extensive fusion of the silver nuclei into larger crystallites before a complete film is formed.

    Original languageEnglish (US)
    Pages (from-to)45-66
    Number of pages22
    JournalSurface Science
    Volume200
    Issue number1
    DOIs
    StatePublished - 1988

    Fingerprint

    Mica
    mica
    Gold
    crystallites
    Surface morphology
    Crystallites
    Microscopes
    microscopes
    gold
    Scanning
    scanning
    topography
    fuses
    Topography
    nuclei
    Electric fuses
    Dislocations (crystals)
    Silver
    Temperature
    silver

    ASJC Scopus subject areas

    • Physical and Theoretical Chemistry
    • Condensed Matter Physics
    • Surfaces and Interfaces

    Cite this

    Chidsey, C. E. D., Loiacono, D. N., Sleator, T., & Nakahara, S. (1988). STM study of the surface morphology of gold on mica. Surface Science, 200(1), 45-66. https://doi.org/10.1016/0039-6028(88)90432-3

    STM study of the surface morphology of gold on mica. / Chidsey, Christopher E D; Loiacono, Dominic N.; Sleator, Tycho; Nakahara, Sho.

    In: Surface Science, Vol. 200, No. 1, 1988, p. 45-66.

    Research output: Contribution to journalArticle

    Chidsey, CED, Loiacono, DN, Sleator, T & Nakahara, S 1988, 'STM study of the surface morphology of gold on mica', Surface Science, vol. 200, no. 1, pp. 45-66. https://doi.org/10.1016/0039-6028(88)90432-3
    Chidsey, Christopher E D ; Loiacono, Dominic N. ; Sleator, Tycho ; Nakahara, Sho. / STM study of the surface morphology of gold on mica. In: Surface Science. 1988 ; Vol. 200, No. 1. pp. 45-66.
    @article{416e4691f9c44bedb46dafcbc059a3b3,
    title = "STM study of the surface morphology of gold on mica",
    abstract = "The scanning tunneling microscope (STM) promises to be a useful tool for the study of thin film deposition processes. We have imaged the growth surface of vapor-deposited gold on mica with an STM. Monatomic steps, dislocations, grain boundaries and grain topographies have been mapped for various gold thicknesses and deposition temperatures. Complementary X-ray diffraction and transmission electron microscopy experiments have been used to determine the orientation, size, shape and defectiveness of the crystallites. Near room temperature, the nuclei do not fuse together into larger single crystallites as the film coalesces, and the mounded topography of the individual crystallites evolves only slightly as the film thickens. The mounds are about 500 {\AA} across and 75 {\AA} high. At higher temperatures (150°C to 300°C), the nuclei apparently fuse as the film coalesces, giving larger crystallites containing holes. The dislocations observed by STM are apparently created as these holes fill in, due to frequent misregistry of the gold lattice around the holes. In the latter stages of deposition, there is a temperature-dependent flattening of the irregular topography caused by the island growth mode, which we attribute to surface diffusion. Consequently, starting the deposition at lower temperatures and increasing the temperature during the deposition gives very flat surfaces. In contrast, depositing gold under the same conditions on a thin underlayer of silver results in large islands separated by grooves, presumably due to extensive fusion of the silver nuclei into larger crystallites before a complete film is formed.",
    author = "Chidsey, {Christopher E D} and Loiacono, {Dominic N.} and Tycho Sleator and Sho Nakahara",
    year = "1988",
    doi = "10.1016/0039-6028(88)90432-3",
    language = "English (US)",
    volume = "200",
    pages = "45--66",
    journal = "Surface Science",
    issn = "0039-6028",
    publisher = "Elsevier",
    number = "1",

    }

    TY - JOUR

    T1 - STM study of the surface morphology of gold on mica

    AU - Chidsey, Christopher E D

    AU - Loiacono, Dominic N.

    AU - Sleator, Tycho

    AU - Nakahara, Sho

    PY - 1988

    Y1 - 1988

    N2 - The scanning tunneling microscope (STM) promises to be a useful tool for the study of thin film deposition processes. We have imaged the growth surface of vapor-deposited gold on mica with an STM. Monatomic steps, dislocations, grain boundaries and grain topographies have been mapped for various gold thicknesses and deposition temperatures. Complementary X-ray diffraction and transmission electron microscopy experiments have been used to determine the orientation, size, shape and defectiveness of the crystallites. Near room temperature, the nuclei do not fuse together into larger single crystallites as the film coalesces, and the mounded topography of the individual crystallites evolves only slightly as the film thickens. The mounds are about 500 Å across and 75 Å high. At higher temperatures (150°C to 300°C), the nuclei apparently fuse as the film coalesces, giving larger crystallites containing holes. The dislocations observed by STM are apparently created as these holes fill in, due to frequent misregistry of the gold lattice around the holes. In the latter stages of deposition, there is a temperature-dependent flattening of the irregular topography caused by the island growth mode, which we attribute to surface diffusion. Consequently, starting the deposition at lower temperatures and increasing the temperature during the deposition gives very flat surfaces. In contrast, depositing gold under the same conditions on a thin underlayer of silver results in large islands separated by grooves, presumably due to extensive fusion of the silver nuclei into larger crystallites before a complete film is formed.

    AB - The scanning tunneling microscope (STM) promises to be a useful tool for the study of thin film deposition processes. We have imaged the growth surface of vapor-deposited gold on mica with an STM. Monatomic steps, dislocations, grain boundaries and grain topographies have been mapped for various gold thicknesses and deposition temperatures. Complementary X-ray diffraction and transmission electron microscopy experiments have been used to determine the orientation, size, shape and defectiveness of the crystallites. Near room temperature, the nuclei do not fuse together into larger single crystallites as the film coalesces, and the mounded topography of the individual crystallites evolves only slightly as the film thickens. The mounds are about 500 Å across and 75 Å high. At higher temperatures (150°C to 300°C), the nuclei apparently fuse as the film coalesces, giving larger crystallites containing holes. The dislocations observed by STM are apparently created as these holes fill in, due to frequent misregistry of the gold lattice around the holes. In the latter stages of deposition, there is a temperature-dependent flattening of the irregular topography caused by the island growth mode, which we attribute to surface diffusion. Consequently, starting the deposition at lower temperatures and increasing the temperature during the deposition gives very flat surfaces. In contrast, depositing gold under the same conditions on a thin underlayer of silver results in large islands separated by grooves, presumably due to extensive fusion of the silver nuclei into larger crystallites before a complete film is formed.

    UR - http://www.scopus.com/inward/record.url?scp=0002516541&partnerID=8YFLogxK

    UR - http://www.scopus.com/inward/citedby.url?scp=0002516541&partnerID=8YFLogxK

    U2 - 10.1016/0039-6028(88)90432-3

    DO - 10.1016/0039-6028(88)90432-3

    M3 - Article

    VL - 200

    SP - 45

    EP - 66

    JO - Surface Science

    JF - Surface Science

    SN - 0039-6028

    IS - 1

    ER -