Improving the damp-heat stability of copper indium gallium diselenide solar cells with a semicrystalline tin dioxide overlayer

B. Selin Tosun, Rebekah K. Feist, Aloysius Gunawan, K. Andre Mkhoyan, Stephen A. Campbell, Eray Aydil

Research output: Contribution to journalArticle

Abstract

While copper indium gallium diselenide (CIGS) thin film solar cells with laboratory efficiencies exceeding 20% have been reported, these high efficiencies may degrade with time as the devices are exposed to humid environments. Specifically, it is well known that water can diffuse to the CIGS-CdS-ZnO heterojunction. This penetration must be reduced or stopped to increase the solar cell lifetime. Herein, we show that tin dioxide layers deposited on top of completed CIGS solar cells can significantly increase the device lifetime by forming a barrier against water diffusion. Specifically, in accelerated damp-heat tests, our best results showed that initially 8-12% efficient CIGS solar cells did not decay from this peak efficiency even after 240 h at 85 °C and 85% relative humidity. In comparison, under identical test conditions, the solar cells without the tin dioxide layer lost nearly 80% of their initial efficiency, within 24 h after commencing the test. We deposited the tin dioxide films by radio frequency magnetron sputtering from tin dioxide targets at 5 mTorr. Semicrystalline SnO 2 films deposited at room temperature had SnO 2 nanocrystals embedded in amorphous SnO 2 without grain boundaries. The semicrystalline films exhibited better damp-heat stability than crystalline films deposited at higher temperature. We infer from the slow open circuit voltage decay that water permeation to the p-n junction is reduced when semicrystalline SnO 2 overlayers are used to protect the solar cell. We attribute this difference in damp heat stability to the lack of grain boundary water diffusion in semicrystalline SnO 2 films.

Original languageEnglish (US)
Pages (from-to)270-276
Number of pages7
JournalSolar Energy Materials and Solar Cells
Volume101
DOIs
StatePublished - Jun 1 2012

Fingerprint

Tin dioxide
Gallium
Indium
Copper
Solar cells
Water
Grain boundaries
Open circuit voltage
Permeation
Magnetron sputtering
Nanocrystals
Heterojunctions
Atmospheric humidity
Hot Temperature
stannic oxide
Crystalline materials
Temperature

Keywords

  • CIGS
  • Damp heat stability
  • Tin dioxide

ASJC Scopus subject areas

  • Renewable Energy, Sustainability and the Environment
  • Electronic, Optical and Magnetic Materials
  • Surfaces, Coatings and Films

Cite this

Improving the damp-heat stability of copper indium gallium diselenide solar cells with a semicrystalline tin dioxide overlayer. / Selin Tosun, B.; Feist, Rebekah K.; Gunawan, Aloysius; Andre Mkhoyan, K.; Campbell, Stephen A.; Aydil, Eray.

In: Solar Energy Materials and Solar Cells, Vol. 101, 01.06.2012, p. 270-276.

Research output: Contribution to journalArticle

Selin Tosun, B. ; Feist, Rebekah K. ; Gunawan, Aloysius ; Andre Mkhoyan, K. ; Campbell, Stephen A. ; Aydil, Eray. / Improving the damp-heat stability of copper indium gallium diselenide solar cells with a semicrystalline tin dioxide overlayer. In: Solar Energy Materials and Solar Cells. 2012 ; Vol. 101. pp. 270-276.
@article{78b61e991a6f4c8bb3cfe01d30740e25,
title = "Improving the damp-heat stability of copper indium gallium diselenide solar cells with a semicrystalline tin dioxide overlayer",
abstract = "While copper indium gallium diselenide (CIGS) thin film solar cells with laboratory efficiencies exceeding 20{\%} have been reported, these high efficiencies may degrade with time as the devices are exposed to humid environments. Specifically, it is well known that water can diffuse to the CIGS-CdS-ZnO heterojunction. This penetration must be reduced or stopped to increase the solar cell lifetime. Herein, we show that tin dioxide layers deposited on top of completed CIGS solar cells can significantly increase the device lifetime by forming a barrier against water diffusion. Specifically, in accelerated damp-heat tests, our best results showed that initially 8-12{\%} efficient CIGS solar cells did not decay from this peak efficiency even after 240 h at 85 °C and 85{\%} relative humidity. In comparison, under identical test conditions, the solar cells without the tin dioxide layer lost nearly 80{\%} of their initial efficiency, within 24 h after commencing the test. We deposited the tin dioxide films by radio frequency magnetron sputtering from tin dioxide targets at 5 mTorr. Semicrystalline SnO 2 films deposited at room temperature had SnO 2 nanocrystals embedded in amorphous SnO 2 without grain boundaries. The semicrystalline films exhibited better damp-heat stability than crystalline films deposited at higher temperature. We infer from the slow open circuit voltage decay that water permeation to the p-n junction is reduced when semicrystalline SnO 2 overlayers are used to protect the solar cell. We attribute this difference in damp heat stability to the lack of grain boundary water diffusion in semicrystalline SnO 2 films.",
keywords = "CIGS, Damp heat stability, Tin dioxide",
author = "{Selin Tosun}, B. and Feist, {Rebekah K.} and Aloysius Gunawan and {Andre Mkhoyan}, K. and Campbell, {Stephen A.} and Eray Aydil",
year = "2012",
month = "6",
day = "1",
doi = "10.1016/j.solmat.2012.02.017",
language = "English (US)",
volume = "101",
pages = "270--276",
journal = "Solar Energy Materials and Solar Cells",
issn = "0927-0248",
publisher = "Elsevier",

}

TY - JOUR

T1 - Improving the damp-heat stability of copper indium gallium diselenide solar cells with a semicrystalline tin dioxide overlayer

AU - Selin Tosun, B.

AU - Feist, Rebekah K.

AU - Gunawan, Aloysius

AU - Andre Mkhoyan, K.

AU - Campbell, Stephen A.

AU - Aydil, Eray

PY - 2012/6/1

Y1 - 2012/6/1

N2 - While copper indium gallium diselenide (CIGS) thin film solar cells with laboratory efficiencies exceeding 20% have been reported, these high efficiencies may degrade with time as the devices are exposed to humid environments. Specifically, it is well known that water can diffuse to the CIGS-CdS-ZnO heterojunction. This penetration must be reduced or stopped to increase the solar cell lifetime. Herein, we show that tin dioxide layers deposited on top of completed CIGS solar cells can significantly increase the device lifetime by forming a barrier against water diffusion. Specifically, in accelerated damp-heat tests, our best results showed that initially 8-12% efficient CIGS solar cells did not decay from this peak efficiency even after 240 h at 85 °C and 85% relative humidity. In comparison, under identical test conditions, the solar cells without the tin dioxide layer lost nearly 80% of their initial efficiency, within 24 h after commencing the test. We deposited the tin dioxide films by radio frequency magnetron sputtering from tin dioxide targets at 5 mTorr. Semicrystalline SnO 2 films deposited at room temperature had SnO 2 nanocrystals embedded in amorphous SnO 2 without grain boundaries. The semicrystalline films exhibited better damp-heat stability than crystalline films deposited at higher temperature. We infer from the slow open circuit voltage decay that water permeation to the p-n junction is reduced when semicrystalline SnO 2 overlayers are used to protect the solar cell. We attribute this difference in damp heat stability to the lack of grain boundary water diffusion in semicrystalline SnO 2 films.

AB - While copper indium gallium diselenide (CIGS) thin film solar cells with laboratory efficiencies exceeding 20% have been reported, these high efficiencies may degrade with time as the devices are exposed to humid environments. Specifically, it is well known that water can diffuse to the CIGS-CdS-ZnO heterojunction. This penetration must be reduced or stopped to increase the solar cell lifetime. Herein, we show that tin dioxide layers deposited on top of completed CIGS solar cells can significantly increase the device lifetime by forming a barrier against water diffusion. Specifically, in accelerated damp-heat tests, our best results showed that initially 8-12% efficient CIGS solar cells did not decay from this peak efficiency even after 240 h at 85 °C and 85% relative humidity. In comparison, under identical test conditions, the solar cells without the tin dioxide layer lost nearly 80% of their initial efficiency, within 24 h after commencing the test. We deposited the tin dioxide films by radio frequency magnetron sputtering from tin dioxide targets at 5 mTorr. Semicrystalline SnO 2 films deposited at room temperature had SnO 2 nanocrystals embedded in amorphous SnO 2 without grain boundaries. The semicrystalline films exhibited better damp-heat stability than crystalline films deposited at higher temperature. We infer from the slow open circuit voltage decay that water permeation to the p-n junction is reduced when semicrystalline SnO 2 overlayers are used to protect the solar cell. We attribute this difference in damp heat stability to the lack of grain boundary water diffusion in semicrystalline SnO 2 films.

KW - CIGS

KW - Damp heat stability

KW - Tin dioxide

UR - http://www.scopus.com/inward/record.url?scp=84859542390&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84859542390&partnerID=8YFLogxK

U2 - 10.1016/j.solmat.2012.02.017

DO - 10.1016/j.solmat.2012.02.017

M3 - Article

VL - 101

SP - 270

EP - 276

JO - Solar Energy Materials and Solar Cells

JF - Solar Energy Materials and Solar Cells

SN - 0927-0248

ER -