Graded structures for all-ceramic restorations

Yu Zhang, H. Chai, B. R. Lawn

Research output: Contribution to journalArticle

Abstract

One failure mode of all-ceramic restorations is radial cracking at the cementation surface, from occlusally induced flexure of the stiffer ceramic layer(s) on the softer dentin underlayer. We hypothesize that such failure may be substantially mitigated by an appropriate grading of elastic modulus through the ceramic thickness. In this study, we fabricated graded structures by infiltrating glass into zirconia plates, with resulting diminished modulus in the outer surfaces. The plates were then bonded to a polymeric base and subjected to flexure by contact loading until fracture. Comparison of infiltrated specimens with non-infiltrated controls showed a significant increase in the fracture loads, by a factor of nearly 2. Finite element analysis revealed the cause of increase in the load-bearing capacity to be diminished tensile stresses within the lower-modulus graded zone, corresponding to an increase in material strength. The results confirmed that suitably graded structures can be highly beneficial in the design of next-generation all-ceramic restorations.

Original languageEnglish (US)
Pages (from-to)417-421
Number of pages5
JournalJournal of Dental Research
Volume89
Issue number4
DOIs
StatePublished - Apr 2010

Fingerprint

Ceramics
Cementation
Finite Element Analysis
Elastic Modulus
Weight-Bearing
Dentin
Glass

Keywords

  • Dental crowns and bridges
  • Fracture
  • Glass-zirconia layers
  • Load-bearing capacity.
  • Modulus gradient

ASJC Scopus subject areas

  • Dentistry(all)

Cite this

Graded structures for all-ceramic restorations. / Zhang, Yu; Chai, H.; Lawn, B. R.

In: Journal of Dental Research, Vol. 89, No. 4, 04.2010, p. 417-421.

Research output: Contribution to journalArticle

Zhang, Yu ; Chai, H. ; Lawn, B. R. / Graded structures for all-ceramic restorations. In: Journal of Dental Research. 2010 ; Vol. 89, No. 4. pp. 417-421.
@article{238caa2bf35549d6a56673d8f58fbac2,
title = "Graded structures for all-ceramic restorations",
abstract = "One failure mode of all-ceramic restorations is radial cracking at the cementation surface, from occlusally induced flexure of the stiffer ceramic layer(s) on the softer dentin underlayer. We hypothesize that such failure may be substantially mitigated by an appropriate grading of elastic modulus through the ceramic thickness. In this study, we fabricated graded structures by infiltrating glass into zirconia plates, with resulting diminished modulus in the outer surfaces. The plates were then bonded to a polymeric base and subjected to flexure by contact loading until fracture. Comparison of infiltrated specimens with non-infiltrated controls showed a significant increase in the fracture loads, by a factor of nearly 2. Finite element analysis revealed the cause of increase in the load-bearing capacity to be diminished tensile stresses within the lower-modulus graded zone, corresponding to an increase in material strength. The results confirmed that suitably graded structures can be highly beneficial in the design of next-generation all-ceramic restorations.",
keywords = "Dental crowns and bridges, Fracture, Glass-zirconia layers, Load-bearing capacity., Modulus gradient",
author = "Yu Zhang and H. Chai and Lawn, {B. R.}",
year = "2010",
month = "4",
doi = "10.1177/0022034510363245",
language = "English (US)",
volume = "89",
pages = "417--421",
journal = "Journal of Dental Research",
issn = "0022-0345",
publisher = "SAGE Publications Inc.",
number = "4",

}

TY - JOUR

T1 - Graded structures for all-ceramic restorations

AU - Zhang, Yu

AU - Chai, H.

AU - Lawn, B. R.

PY - 2010/4

Y1 - 2010/4

N2 - One failure mode of all-ceramic restorations is radial cracking at the cementation surface, from occlusally induced flexure of the stiffer ceramic layer(s) on the softer dentin underlayer. We hypothesize that such failure may be substantially mitigated by an appropriate grading of elastic modulus through the ceramic thickness. In this study, we fabricated graded structures by infiltrating glass into zirconia plates, with resulting diminished modulus in the outer surfaces. The plates were then bonded to a polymeric base and subjected to flexure by contact loading until fracture. Comparison of infiltrated specimens with non-infiltrated controls showed a significant increase in the fracture loads, by a factor of nearly 2. Finite element analysis revealed the cause of increase in the load-bearing capacity to be diminished tensile stresses within the lower-modulus graded zone, corresponding to an increase in material strength. The results confirmed that suitably graded structures can be highly beneficial in the design of next-generation all-ceramic restorations.

AB - One failure mode of all-ceramic restorations is radial cracking at the cementation surface, from occlusally induced flexure of the stiffer ceramic layer(s) on the softer dentin underlayer. We hypothesize that such failure may be substantially mitigated by an appropriate grading of elastic modulus through the ceramic thickness. In this study, we fabricated graded structures by infiltrating glass into zirconia plates, with resulting diminished modulus in the outer surfaces. The plates were then bonded to a polymeric base and subjected to flexure by contact loading until fracture. Comparison of infiltrated specimens with non-infiltrated controls showed a significant increase in the fracture loads, by a factor of nearly 2. Finite element analysis revealed the cause of increase in the load-bearing capacity to be diminished tensile stresses within the lower-modulus graded zone, corresponding to an increase in material strength. The results confirmed that suitably graded structures can be highly beneficial in the design of next-generation all-ceramic restorations.

KW - Dental crowns and bridges

KW - Fracture

KW - Glass-zirconia layers

KW - Load-bearing capacity.

KW - Modulus gradient

UR - http://www.scopus.com/inward/record.url?scp=77949618561&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=77949618561&partnerID=8YFLogxK

U2 - 10.1177/0022034510363245

DO - 10.1177/0022034510363245

M3 - Article

VL - 89

SP - 417

EP - 421

JO - Journal of Dental Research

JF - Journal of Dental Research

SN - 0022-0345

IS - 4

ER -