Anisotropy and coercivity of Co-Pt films electrodeposited onto oriented ruthenium

Elian Xu, Gyana Pattanaik, Giovanni Zangari, James Weston

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

Co-rich Co-Pt films (thickness 5 - 1000 nm) were electrodeposited under galvanostatic conditions onto (0001)-oriented ruthenium seed layers. The films grow mainly with a hexagonal close packed structure, with the c axis oriented perpendicular to the film plane The growth occurs epitaxially on top of the Ru seed, and thin films reproduce the grain size and morphology of the seed layer. Thick films grow with a columnar microstructure; the extent of coarsening of the column diameter depends on the growth rate and becomes negligible for current densities above 50 mA/cm2. The films exhibit a perpendicular magnetic anisotropy, and the magnetic properties depend on thickness and growth rate. Films grown at low rate present lower coercivity; the high coercivity observed in films grown at high rate is attributed to the formation of defects during growth. At large thickness, the magnetic properties are dominated by the demagnetizing fields. copyright The Electrochemical Society.

Original languageEnglish (US)
Title of host publicationECS Transactions - 9th International Symposium on Magnetic Materials, Processes and Devices
Pages289-296
Number of pages8
Volume3
Edition25
DOIs
StatePublished - Dec 1 2007
Event9th International Symposium on Magnetic Materials, Processes and Devices - 210th ECS Meeting - Cancun, Mexico
Duration: Oct 31 2006Nov 2 2006

Conference

Conference9th International Symposium on Magnetic Materials, Processes and Devices - 210th ECS Meeting
CountryMexico
CityCancun
Period10/31/0611/2/06

Fingerprint

Coercive force
Ruthenium
Anisotropy
Seed
Magnetic properties
Magnetic anisotropy
Coarsening
Thick films
Film thickness
Current density
Thin films
Defects
Microstructure

ASJC Scopus subject areas

  • Engineering(all)

Cite this

Xu, E., Pattanaik, G., Zangari, G., & Weston, J. (2007). Anisotropy and coercivity of Co-Pt films electrodeposited onto oriented ruthenium. In ECS Transactions - 9th International Symposium on Magnetic Materials, Processes and Devices (25 ed., Vol. 3, pp. 289-296) https://doi.org/10.1149/1.2753261

Anisotropy and coercivity of Co-Pt films electrodeposited onto oriented ruthenium. / Xu, Elian; Pattanaik, Gyana; Zangari, Giovanni; Weston, James.

ECS Transactions - 9th International Symposium on Magnetic Materials, Processes and Devices. Vol. 3 25. ed. 2007. p. 289-296.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Xu, E, Pattanaik, G, Zangari, G & Weston, J 2007, Anisotropy and coercivity of Co-Pt films electrodeposited onto oriented ruthenium. in ECS Transactions - 9th International Symposium on Magnetic Materials, Processes and Devices. 25 edn, vol. 3, pp. 289-296, 9th International Symposium on Magnetic Materials, Processes and Devices - 210th ECS Meeting, Cancun, Mexico, 10/31/06. https://doi.org/10.1149/1.2753261
Xu E, Pattanaik G, Zangari G, Weston J. Anisotropy and coercivity of Co-Pt films electrodeposited onto oriented ruthenium. In ECS Transactions - 9th International Symposium on Magnetic Materials, Processes and Devices. 25 ed. Vol. 3. 2007. p. 289-296 https://doi.org/10.1149/1.2753261
Xu, Elian ; Pattanaik, Gyana ; Zangari, Giovanni ; Weston, James. / Anisotropy and coercivity of Co-Pt films electrodeposited onto oriented ruthenium. ECS Transactions - 9th International Symposium on Magnetic Materials, Processes and Devices. Vol. 3 25. ed. 2007. pp. 289-296
@inproceedings{b11a1ca2f1964368aba084bc09f1c5ae,
title = "Anisotropy and coercivity of Co-Pt films electrodeposited onto oriented ruthenium",
abstract = "Co-rich Co-Pt films (thickness 5 - 1000 nm) were electrodeposited under galvanostatic conditions onto (0001)-oriented ruthenium seed layers. The films grow mainly with a hexagonal close packed structure, with the c axis oriented perpendicular to the film plane The growth occurs epitaxially on top of the Ru seed, and thin films reproduce the grain size and morphology of the seed layer. Thick films grow with a columnar microstructure; the extent of coarsening of the column diameter depends on the growth rate and becomes negligible for current densities above 50 mA/cm2. The films exhibit a perpendicular magnetic anisotropy, and the magnetic properties depend on thickness and growth rate. Films grown at low rate present lower coercivity; the high coercivity observed in films grown at high rate is attributed to the formation of defects during growth. At large thickness, the magnetic properties are dominated by the demagnetizing fields. copyright The Electrochemical Society.",
author = "Elian Xu and Gyana Pattanaik and Giovanni Zangari and James Weston",
year = "2007",
month = "12",
day = "1",
doi = "10.1149/1.2753261",
language = "English (US)",
isbn = "9781566775601",
volume = "3",
pages = "289--296",
booktitle = "ECS Transactions - 9th International Symposium on Magnetic Materials, Processes and Devices",
edition = "25",

}

TY - GEN

T1 - Anisotropy and coercivity of Co-Pt films electrodeposited onto oriented ruthenium

AU - Xu, Elian

AU - Pattanaik, Gyana

AU - Zangari, Giovanni

AU - Weston, James

PY - 2007/12/1

Y1 - 2007/12/1

N2 - Co-rich Co-Pt films (thickness 5 - 1000 nm) were electrodeposited under galvanostatic conditions onto (0001)-oriented ruthenium seed layers. The films grow mainly with a hexagonal close packed structure, with the c axis oriented perpendicular to the film plane The growth occurs epitaxially on top of the Ru seed, and thin films reproduce the grain size and morphology of the seed layer. Thick films grow with a columnar microstructure; the extent of coarsening of the column diameter depends on the growth rate and becomes negligible for current densities above 50 mA/cm2. The films exhibit a perpendicular magnetic anisotropy, and the magnetic properties depend on thickness and growth rate. Films grown at low rate present lower coercivity; the high coercivity observed in films grown at high rate is attributed to the formation of defects during growth. At large thickness, the magnetic properties are dominated by the demagnetizing fields. copyright The Electrochemical Society.

AB - Co-rich Co-Pt films (thickness 5 - 1000 nm) were electrodeposited under galvanostatic conditions onto (0001)-oriented ruthenium seed layers. The films grow mainly with a hexagonal close packed structure, with the c axis oriented perpendicular to the film plane The growth occurs epitaxially on top of the Ru seed, and thin films reproduce the grain size and morphology of the seed layer. Thick films grow with a columnar microstructure; the extent of coarsening of the column diameter depends on the growth rate and becomes negligible for current densities above 50 mA/cm2. The films exhibit a perpendicular magnetic anisotropy, and the magnetic properties depend on thickness and growth rate. Films grown at low rate present lower coercivity; the high coercivity observed in films grown at high rate is attributed to the formation of defects during growth. At large thickness, the magnetic properties are dominated by the demagnetizing fields. copyright The Electrochemical Society.

UR - http://www.scopus.com/inward/record.url?scp=45249092765&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=45249092765&partnerID=8YFLogxK

U2 - 10.1149/1.2753261

DO - 10.1149/1.2753261

M3 - Conference contribution

AN - SCOPUS:45249092765

SN - 9781566775601

VL - 3

SP - 289

EP - 296

BT - ECS Transactions - 9th International Symposium on Magnetic Materials, Processes and Devices

ER -